SnO2-ThO2-PdCl2-In2O3 gas sensing ceramic systems were studied in order to lowr the operating temperatures and reduce the dependence of ambient temperatures and humidities. Sensing materials were coated by brush on the alumina tube followed by the impregnation of solidfier(ethylsilicate). Coated species were dried and sintered at 75$0^{circ}C$ for 30min. carbon monoxide gas detecting sensitiviteis were measured in various ambinet temperatures and humidities. In the composition of 94SnO2-5ThO2-PdCl2 system carbon monoxide gas detecting sensors showed the highest detecting sensitivities and the lowest operating temperature(15$0^{circ}C$). As the ambient temperatures and humidities were increased, sensitivities were decreased. Because the oscillation effects were observed at high humidities, it was suggested that the sensitivities of sensors depend greatly on the humidities.