ZrO2 fine powders were prepared by hydrolysis, adding 0.1, 0.2, 0.3, 0.4, 0.5, 0.6mol/1H2O/ethanol to 0.1 mol/l Zr(OC3H7)4/ethanol. When hydrolized by adding 0.1mol/l Zr(OC3H7)4/ethanol to 0.1, 0.2mol/l H2O/ethanol., spherical monodispersed ZrO2 fine powders were obtained. And in this condition average sizes were about 0.5, 0.3${mu}{ extrm}{m}$, respectively. The more H2O/ethanol concentration increased, the more the particle size decreased and the particles were agglomerated strongly. Prepared powders were amorphous and hydrates. The calcined powders with 43$0^{circ}C$ and 100$0^{circ}C$ were showed tetragonal and monoclinic phase, respectively.