Effects of temperature on the tensile properties of annealed and hydirded Zircaloy-4 plate in which hydrides are precitated paralled to the rolling direction were investigated. The main results obtained are as follows : 1) In annealed Zircaloy-4, yield point phenomenon was found in the temperature range of $200-550^{circ}C$, while in hydrided alloy the phenomenon was found in the range of $200-400^{circ}C$. 2) The dynamic strain aging behavior was occurd in the temperature interval of 400-$550^{circ}C$in both annealed and hydrided Zircaloy-4. 3) The nearly values of yield strength, tensile stength and elongation are obtained in both annealed and hydried Zircaloy-4. From this result, we are led to conclude that the hydrides which are preiptated parallel to the circumferenial direction of nucler fuel are not so harmful for tensile properties of the clad.