The water-vapor sorption isotherms of viscose rayon and of modified viscose rayon were studied to elucidate the change of sorptivity by the DMDHEU resin finish. To determine the sorption isotherms, moisture regains of the samples were measured at various humidities. The sorption isotherms were determined by the BET and GAB multilayer adsorption theories. The adsorption isotherm of the starting rayon was Brunauer Type II while with increasing resin content those of the DMDHEU-treated rayon became progressively more like Type IV. The DMDHEU-treated samples appeared to be hydrophilic due to the hydrophilicity of DMDHEU although moisture regains at higher humidities markedly decreased because of an impediment in swelling by crosslinkings. The $W_{m}$ value and surface area of crosslinked samples increased with increasing resin content. VR-R-6 which was the most heavily crosslinked viscose rayon had the highest $W_{m}$ and surface area values among all the samples. Relative sorption hysteresis was decreased as humidity increased for all samples. The untreated viscose rayon appeared to have a higher value than the DMDHEU-treated rayon.