The plane strain fracture toughness of a material characterize the resistance to fracture in the presence of a sharp crack under severe tensile condition. Fracture toughness can be determined by indentation method. The purpose of this study was to investigate the fracture toughness of dental amalgams by measuring the plane strain fracture toughness and the fracture toughness from indentation method. Two conventional and four high copper amalgam alloys were employed for this study. The amalgams were prepared according to the A.D.A. spec. No. 1 and inserted into the specially designed mould with the single edge notch specimen to use in 3-point bending method. The specimens (20mm long, 4mm wide, 2mm thick) were stored at $37^{circ}C$ for 1 week, and tested in 3-point bending by means of Instron at a cross-head speed of 1mm/min. In indentation method, the specimens were made in same manner as single edge notch specimens. The test was conducted with Vickers hardness tester at 10kg load. The following results were obtained. 1. The plane strain fracture toughness and the fracture toughness from indentation method were higher in the low copper amalgams than the high copper amalgams. 2. In high copper amalgams, the fracture toughness of amalgams decreases according as the copper contents increase. 3. In similar copper contents, the single composition amalgams have a higher fracture toughness than the admixed amalgams.