The purpose of this study was to evaluate the effects of dentin adhesives(Gluma$^{(R)}$ and Scotchbond 2$^{(R)}$) on the marginal adaptation of light cured composite resin (Heliosit$^{(R)}$) by using SEM. The recently extracted 30 teeth were used and round cavities were prepared on the occlusal surfaces of the teeth with predesigned depth and diameter. The teeth were divided into three groups. Group 1 : Gluma$^{(R)}$ + Heliosit$^{(R)}$ Group 2 : Scotchbond 2$^{(R)}$ + Heliosit$^{(R)}$ Group 3 : Enamelbond$^{(R)}$ + Heliosit$^{(R)}$ Filling with Heliosit, the teeth were stored in saline solution for 24 hours. After the thermocycling procedure, the teeth were cut vertically into the restorations. The SEM observation was carried out to evaluate the marginal adaptation of the composite resin. The following results were obtained. The following results were obtained. 1. The groups using Gluma$^{(R)}$ and Scotchbond 2$^{(R)}$ showed better than the control group on marginal adaptation to the dentin. 2. The group using Gluma$^{(R)}$ was superior to the group using Scotchbond 2$^{(R)}$, but the difference was not significant. 3. In all groups, the marginal gaps were wider on the pulpal walls than on the lateral walls of restorations.