The Plasma Arc Cutting Method using high density and hight temperature beam is well applicable to the cutting of the nonferrous metal (Al alloy ) and stainless steel which are unable to be cut by the use of the oxy-fuel gas. This study focalizes on the cutting phenomena of the plate of (mm) thickness, since the cutting phenomena of thick plates have been rather thoroughly studied. In this study the cutting groove, adhesive phenomena of dross, surface roughness were measured according to the variation of cutting speed and compared with the case of mild steel plates. The result showed that the kerf width variation of Al alloy was similar to the case of mild steel, while that of the stainless steel differed from the mild steel. In the adhesive phenomena of dross, 6(mm) thick plates of Al alloy showed a difference from those of thick plates, but the stainless steel was similar to thick plates. The surface roughness variation of Al alloy wias minimum at 67 cm/min, while that of stainless steel was at 30cm/min.