The tin-lead alloy was electrodeposited in the low range of peak current density in order to investigate the change of composition and microstructure of them. The Pb content of alloy deposits, which was decreased with increasing average current density, was relatively lower than that of D.C. plated alloy deposit. The preferred orientation of alloy deposit was changed with increasing peak current density and the surface morphology of alloy deposits was closely related to the preferred orientation of them.