The effects of silicone contents and flow rates(agitation rates) of electrolyte on the formation and mechanical properties of hard anodized film of Al-Si alloy have been studied in 12% H2SO4 + 1% Oxalic acid with varying the silicone contents in the rance of 0 to 11.6% and the flow rates of electrolyte in the range of 0 to 90cm/sec. The film forming voltage required to maintain an equivalent current density significantly increase with the silicone content of Al-Si alloys due to a low conductivity of silicone. Hardness and wear resistance of the anodized film of Al-Si alloys decreases wit increasing the silicone content. The increase in the flow rate of electrolyte has a similar influence on the formation and mechanical properties of anodized film as does the decrease in bath temperature. Hardness of anodized film is rapidly increased with the flow rate being increased from 10cm/sec. It is observed that the increase in the flow rate from 11cm/sec. It is observed that the increase in the flow from 11cm/sec to 48cm/sec is more effective in enhancing the hardness of film than is the decrease in bath temperature from 1$0^{circ}C$ to $0^{circ}C$.