In this study we have investigated the sealing characteristics of glasses suitable for producing the magnetic gap of the ferrite head cores which have been widely used for VTR and computer magnetic heads. $PbO-B_2O_3$ g1asses were evaluated by measuring microhardness, thermal expansion coefficient and sliding wear resistance. Concentration distribution of elements at the interface was observed by WDS. wettability was measured by high temperature microscopy. The results were as follows ; 1. In sealing glasses of $PbO-B_2O_3$ system, thermal expansion coefficient and wear volume were increased with increasing PbO content, and were decreased with increasing $B_2O_3$ content. 2. The contact angle of $PbO-B_2O_3$ Systems was mainly influenced by PbO content. 3. The sealing temperature showed a tendency to decrease proportionally with the increase of the coefficient of thermal expansion. 4. The diffusion at the interface between Mn-Zn single crystal ferrite and sealing glasses of $PbO-B_2O_3$ system was dominated by small amount of diffusion of ferrite content into glass part, which was very little affected by sealing heat treatment time.