In this study, the structural phase transition and decomposition of superconducting ceramic, Y-Ba-Cu-O system was studied. The results of the study are as follows. The high Tc superconductor $Y_2Ba_2Cu_3O_{7-x}$ is made in solid state reaction of $O_2$ atmosphere and the valve of X in $Y_2Ba_2Cu_3O_{7-x}$ is 0.1~0.2. The transition temperature of tetragonal-orthorhombic phase of $Y_2Ba_2Cu_3O_{7-x}$ appear at $790^{circ}C-900^{circ}C$. In the result of measuring the electrical resistance of sample annealed in $O_2$ atmosphere, the electrical resistance show zero at 92 K and the best superconductor, $Y_2Ba_2Cu_3O_{7-x}$(Y 123) can be mabe.