The Purpose of this study was to evaluate the marginal fit of ceramo-metal crown according to the different ceramo-metal alloy types and the curvature of labio-cervical margin. Degudent $G^{(R)}$ as precious and $Verabond^{(R)}$ as non-precious ceramo-metal alloy were used. The abutment was preparaed with two different curvature types : a normal curvature type and a pronounced curvature type. 20 crowns were farbricated using four different combinations and their marginal fits were measured at 3 consecutive stages (before degassing, after degassing, after glazing) using microscope under 200 magnification. The results were as follows: 1 . Marginal fitness before degassing. The groups of precious ceramo-metal exhibited better marginal fit than the groups of non-precious ceramo-metal with significant difference(P<0.05) . In the same ceramo-metal groups, the normal curvature group exhibited better marginal fit than the pronounced curvature group but without significant difference(P>0.05). 2. Marginal fitness after degassing. By degassing, the group of pronounced curvature and non-precious ceramo-metal was deformed the most, and the degree of margin fitness of each group was the same as before degassing. 3. Marginal fitness after glazing The group of normal curvature and precious ceramo-metal exhibited better marginal fit than the group of pronounced curvature and non-precious ceramo-metal with significant difference(P>0.05), and the degree of margin fitness of each group was the same as before degassing.