The purpose of this study was to determine the optimum range of laser energy density to the enamel surface of permanent incisors when they are irradiated with the pulsed Nd : YAG laser, Laser impacts on each experimental group were made at energy density of $20sim50J/cm^2$ by 20 pulses of the pulse width 1.2 msec. The author investigated the enamel surface with the sunning electron microscope(SEM) and the surface roughness tester, and measured the shear bond strength between electrolytically etched Ni-Cr-Be alloy casting and composite resin. The obtained results were as follows: 1. The surface roughness of enamel after laser irradiation showed the significant difference level from the energy density $40J/cm^2(P<0.05)$. 2. The mean shear bond strength of etched-metal resin-bonded specimens were $154.23{pm}33.30kg/cm^2$ at unlased enamel surface and $195.72{pm}29.56kg/cm^2$ at lased energy density $30J/cm^2$, and showed a significant difference(P<0.05). 8. SEM photographs showed the irregular microcracks and the structural changes of lased enamel surface. 4. SEM photographs of the fracture surface after testing the shear bond strength showed the aspect of interfacial fracture between bonding agent and composite resin at the metal sides.