When the porcelain fused to metal restorations were fractured at the metal interface, various techniques and materials for intraoral porcelain repair have been suggested. The purpose of this study was to investigate the effect of metal surface treatment method and water storage on the shear bond strength of four porcelain repair systems. : Clearfil(Kuraray), All-bond(Bisco), Superbond C & B(Sun Medical), Panavia OP(Kuraray). After the metal surfaces of the specimens were sandblasted by aluminum oxide or roughened by diamond point, they were stored in double deionized water(24 Hr., $37^{circ}C$) and thermocycling was performed(24 Hr., 1024 cycles), and again half of specimes were stored in water bath(2 Months, $37^{circ}C$). Mean shear bond strength and mode of failure were recorded. The results of this study were obtained as follows : 1. Differences were observed between the sandblasted and diamond - treated specimens in Clearfil, All-bond, and Superbond. No statistically significant differences were observed in Panavia. 2. The 2-month storage time significantly affected the bond strength of All-bond and Superbond. No statistically significant differences were observed in Clearfil and Panavia. 3. The failures were observed at the interface between opaque resin and the metal in Clearfil and All-bond. 4. The failures were observed at the interface between opaque resin and veneered resin in Panavia. The failures were observed at the interface between opaque resin and veneered resin in Superbond, but 40% of them were fractured at the interface between the metal and opaque resin after 2-month storage time.