In recent years immediate implantation has been tried by a few clinicians. This study placed IMZ implants in the rabbit femur with and without bony defects around the implant for simulating fresh extraction site. And one group with bony defects used porous hydroxyapatite ganules(HA) to fill if and the other group left the bony defects around the implant. The purpose of this study was to compare the shear bond strength and the bony contact and formation around the implant. Fifteen rabbits were divided into three groups and placed 10 IMZ implants to each group. Implant sites were surgically prepared with IMZ drills kit and implants were placed(Control), artificial bony defect was created with Apaceram drills kit around the implant sites and implants were placed(Experimental I), bony defect was filled with porous hydroxyapatite granules(Experimental II). Thereafter, rabbits were sacrificed at 8th week and specimens were prepared and pushout tested for shear bond strength of bone-implant interface immediately. Undecalcified and decalcified specimens were prepared with Vilanueva and hematoxylin-eosin stain for light microscopic finding. The results of this study were as follows. 1. In the control group, mean shear strength of bone-implant interface was $2.614{pm}0.680$ MPa, experimental I was $0.664{pm}0.322$ MPa, and experimental II was $2.281{pm}0.606$ MPa. There was significant difference between control and experimental I, between experimental I and experimental II, but did not show significant difference between control and experimental II statistically. 2. In the bony formation surrounding IMZ implant of the three groups, that of cortical bone is more advanced than cancellous bone area. 3. In the histological findings of undecalcified specimens, control and experimental II showed more than 50% of bony or osteoid formation at the bony-implant interface. 4. In the histological findings of undecalcified specimens, experimental I showed less than 50% of bony or osteoid formation at the interface, and observed partial bony defect in the coronal zone. 5. In the experimental II group, were observed direct bony contact to hydroxyapatite granules, and infiltration of a few giant cells. 6. No inflammatory responses were seen around the titanium implants and the hydroxyapatite granules.