To investigate the delignification behaviour in solvolysis pulping process, Populus alba ${ imes}$ glandulosa H. and Pinus Kuraiensis S. et Z. were cooked with p-cresol and vater solvent(2:8, 5:5, 8:2 v/v) at $175^{circ}C$ for 9 cooking time levels(20, 40, 60, 80, 100, 120, 140, 160, 180, min). Pulp yield, residual lignin content, de lignification rate, decarborhydration rate were determined. Delignification behaviours were analyzed by TEM. 1. The p-cresol-water solvent cooking of P. alba ${ imes}$ glandulosa showed good delignification at the solvent system which the mixture ratio of p-cresol and water were 2:8(v/v), while the cooking of P. koraiensis with the p-cresol and water mixture ratio of 5:5 was no good. 2. P. alba ${ imes}$ glandulosa showed three step-delignification phenomena at the solvent system which the mixture ratio of p-cresol and water were 2:8(v/v) anti 5:5(v/v). But P. koraiensis showed a first order delignification reaction at the same mixture ratio of p-cresol and water solvent system. 3. In TEM micrograph obtained for the solvent system which the mixture ratio of p-cresol and water was 5:5(v/v), the partial delignification of the cell corner of P. alba ${ imes}$ glandulosa and P. koraiensis were observed at 60min. of cooking time. Complete delignification at the cell corner of P. alba ${ imes}$ glandulosa was observed at 160min. and that of P. koraiensis was observed of 180min. of cooking time. 4. In optical microscopic observation, fiber separation of P. alba ${ imes}$ glandulosa occured at 120min. and that of P. koraiensis began at 140min. of cooking time. 5. At the solvent system which the mixture ratio of p-cresol and water was 5:5(v/v), middle layer on secondary wall($S_2$) and cell corner of P. alba ${ imes}$ glandulosa were more selectively delignified than primary wall(P) and outer layer on secondary wall($S_1$). However P. koraiensis did not showed any difference in delignification between cell wall layers and cell corner.