In this study, the relative effectiveness of antimony trioxide-containing coat on fire retardancy of plywood, particleboard and medium density fiberboard was investigated and compared through ISO ignition test and inclined panel test with non-coated ones. The results obtained were summarized as fallows: Any treated materials was not ignited in inclined panel test with 5 minutes, but only particleboard among treated ones burned in ISO ignition test with fairly delayed time. The weight loss rate of plywood decreased with the increased addition level of fire-retardant and the least values were obtained in particleboard and MDF at addition level of 7% and 5% respectively. Carbonized area of wood based materials decreased with the increased addition level of fire retardant. The temperatures of back in plywood, particleboard treated with fire-retard ant coat containing 7% $Sb_2O_3$ showed the lowest but MDF did not show any effectiveness with the increased addition level. The first flash time of plywood treated with fire retardant coat containing 9% $Sb_2O_3$, MDF and particleboard treated with fire retardant coat containing 7% $Sb_2O_3$ were 257sec., 286.4sec., 165.4sec. respectively.