This study was carried out to investigate the fracture behavior and the fracture criterion of yellow lauan(Shorea spp.), when has used for furniture and wood structures, and to offer a reliability for wood structure and basic data for wood fracture criterion in experiments which are fracture tested under mode I, mode II and mixed mode loading condition. The results were summarized as follows; 1. Fractures in specimens which have inclined grain in yellow lauan procedeed from crack tip in the radial direction along the grain. 2. In yellow lauan, $K_{IC}RL$ was 42.1kg/$cm^{3/2}$ and $K_{IIC}RL$ was 15.8kg/$cm^{3/2}$. 3. The fracture criteria of lauan were; ($K_I/K_{IC}$)+($K_{II}/K_{IIC}$)=1 in RL system with inclined grain at $45^{circ}$, ($K_I/K_{IC}$)+$(K_{II}/K_{IIC})^2$=1 with inclined grain at $15^{circ}$ and $(K_I/K_{IC})^2$+$(K_{II}/K_{IIC})^2$=1 with inclined grain at $30^{circ}$, $60^{circ}$, $75^{circ}$ and $90^{circ}$, respectively. 4. The fracture criterion of wood could vary with the species, and the load applying condition. In order to measure the fracture criterion strictly, along with standardization of specimen geometry a large amount of experimental data is needed. 5. $K_{IC}$(critical stress intensity factor) can be predicted by grain angle. As the grain inclined angle increased, $K_{IC}$ and $K_{IIC}$ are increased.