Diffusion bonding of Mo was performed by using the metallic coating of Cu and Cr on the surface to be bonded. Joint characteristics of Mo with or without coating layer were compared in metallurgical and fractograpical aspects. The results showed that the diffusion bonding with coating layer, especially with Cu coating, increased the bending strength of joint. Variation of heating cycle(elevation of temperature for a moment) did not affect significantly the mechanical properties of joint. Fractographical analysis showed that the fracture of joint bonded with Cr coating occurred at the coating layer, while that with Cu coating occurred at the base metal.