A significant drag reduction in the turbulent flow of CWM(coal Water Mixture) adding minute amounts of high molecular weight polymer additives has been obtained and it was compared with pure CWM.However, the rate of drag reduction could come down with flow time, which is caused by polymer degradation, The rate of drag reduction and polymer degradation is affected by polymer type, concentration, molecular weight, and flow velocity. In the present investigation, these important parameters were evaluated for their influences on polymer degradation in order to find out stable conditions for CWM transportation with time. It was necessary to determine the more effective type of polymer additives to guarantee the optimum conditions for CWM transport. Experiments were undertaken with a test section of pipe diameter 9.8mm and pipe length 3500mm(L/D=357) in a closed loop, and polyacrylamide and polyetylene oxide were utilized as polymer additives. The tests were carried out under the conditions of 200, 400, 700ppm of polymer concentrations. CWM concentrations utilized were 5% and 10% with flow velocities of 4.9m/s and 6.1m/s. Experimental data show that polyehylene oxide degraded faster than polyacrylamide in CWM transport, and polyacryamide is considered to be a more effective candidate as additive for long time-CWM transport. Polymer degradation is also found to be more likely at lower polymer concentrations, at higher flow velocities, and higher CWM concentrations.