KTiOP04 is a nonlinear optical crystal which is most widely used for frequency doubling of the radiation of Nd : YAG laser. In the experiment, sin ale crystals of KTiOP04 were grown by TSSG technique using 3K2W04·P2O5 flux. Low temperature gradient furnace suitable for KTP single crystal growth was used. Seed crystal was placed at the surface of the solution for the purpose of better observation of the growing crystals and the possibility of diameter control. Solution included 66.7mol% KTiOP04 for all experiments and its saturation temperature was 1020℃. The conditions of single crystal growth were as follows: cooling rate 0.2℃/h, crystal rotation rate 50rpm, c -axis seed. Using these conditions, single crystals up to 23 ×25×25mm3 have been groan from about 100cc solution. We have also observed a change in the crystal growth habit which resulted in the formation of large (201) faces and small (100) faces. And some crystals have (101) faces.