Flexural strength, microstructure, hydration reaction and moisture sensitivity in macro defect-free (MDF) cement, which basically prepared of high alumina cement (HAC) and hydroxypropyl methylcellulose (HPMC) and polyvinylalcohol (PVA) as water soluble polymer were investigated. Cement composites based on HAC-PVA system were improved in flexural strength than that of HAC-HPMC system especially, the strength of specimens added to 10 wt% of polyvinylalcohol was 160 MPa. These improvements of flexural strength were attributed to not only the effect of water soluble polymer in elimination of macropores (above 100 $mu extrm{m}$) and cement grain bridging, but the effect of unhydrate cement as an aggregate. Moisture sensitivity and flexural strength in wet condition of MDF cement composites immersed in water at 80$^{circ}C$ for 3 days were decreased.