Carbon solid was prepared from dormant mesophase pitch (DMPP) without using a binder and its properties were characterized. DMPP powder was stabilized with air or nitric acid in pretreatment stage so that it might not soften in later heat ttreatment stage. Optimum sintering properties were obtained from carbon powder with 2.36∼2.38 of C/H atomic ratio and 1.27∼1.40 of C/O atomic ration in air stabilization. In nitric acid stabilization, optimum sintering properties were obtained when 20∼40 vol.% of nitric acid solution was used. Compressive strength increased up to 1200$^{circ}C$ of heat treatment temperature, and the highest compressive strength and bulk density of carbon solid from DMPP were 3000 kgf/㎤, respectively. The optical properties of carbon solid obtained was fine mosaic structure. Carbon solid after graphitization showed the properties of hard carbon due to stabilization and its shore hardness was 120.