Lead lanthanum zirconate titanate (PLZT, 6/65/35) powders, crack-free and dense thin films have been prepared by polymeric sol-gel process. Pyrolysis of the gel, crystallization and optical transmittance behavior of the PLZT thin film onto sapphire substrate have been studied. Esterification occurs during synthesis of PLZT complexation. Crystalline Pb phase was transiently formed near 450$^{circ}C$. Content of perovskite phase in the films were increased with increasing thickness of film, but the kinetics of formation of perovskite phase in films was slower than that of powders. Transmittance of the films was decreased with increasing the temperature of heat treatment. Ferroelectric hysteresis loop measurements indicated increments of remanent polarization and coercive field for plenty more of perovskite phase.