Chemical vapor deposition of ATO from SnCl4-SbCl5-H2O gas mixture was investigated with thermodynamic and experimental analyses. Electrical conductivity of the ATO film was much improved under deposition conditions of low input-gas ratio, Psbcl5/Psbcl4. This increase of the conductivity was attributed to donor electrons produced mainly by the pentavalent Sb ions in SnO2 lattice. However high input-gas ratio conditions produced an ATO film consisting of a mixture of SnO2 and very fine Sb2O5 phase. It was found that the deterioration of electrical conductivity and optical transmission of the film was caused by the deposition of fine Sb2O5 phase in the SnO2 matrix.