An analytical scheme for predicting the crack aspect pattern of materials which contain twin surface cracks was developed. Fatigue tests were performed on twin surface cracked PMMA plate specimens to obtain the interaction factor accounting for the interference effect of adjacent cracks. Here, the interaction factor is defined as the ratio of the stress intensity factor for twin surface cracks to that for a single surface crack. From the analysis of the fatigue test result, the interaction factor was presented as the ninth-order polynomial expression having a function of dimensionless crack spacing ratio. Then the polynomial expression was incorporated into the prediction program of the crack aspect pattern for twin surface cracked materials. And, the interaction effect and the coalescence condition of adjacent cracks were simplified in the newly developed prediction scheme of the crack aspect pattern. The predicted crack growth pattern using the prediction scheme was compared with test data from PMMA specimen. The predicted pattern agreed well with the test data.