Treatment of vinyl monomers onto silk fiber modifies the properties of the original silk fiber considerably. This field has been the subject of investigation by many workers using chemical and radiation initiation. Many studies on the reaction conditions, polymerization mechanism, physical properties and practical performances of methacrylamide-treated silk fiber have been continued. However, the polymerization mechanism has not been clearly revealed yet and this remains ambiguously whether the grafting is formed on fiber or not. In general, it has been accepted that free radicals were formed and vinyl monomers were polymerized in silk fibroin by graft polymerization mechanism, while active sties were varied by the types of monomer and initiator as well as by the reaction conditions. On the other hand, there is another argument on polymerization mechanism, in which monomers are polymerized and impregnated in the internal side of the fiber by homopolymerization. Though a large number of analytical methods are used to examine the polymerization mechanism of methacrylamide-treated silk fiber, the results on the basis of thermal analysis are merely reported in this paper. In differential scanning calorimetry (DSC) analysis, the thermal decomposition behaviors of the methacrylamie-treated silk fibers were determined and compared to those of the controlled silk fibers. DSC curves obtained from the methacrylamide-treated silk fibers showed double peaks at around 290$^{circ}C$ (A peak) and 320$^{circ}C$ (B peak) which are attributed to the thermal decomposition of the methacrylamide polymer and silk fibroin fiber, respectively. The temperature of A and B peak shifted to higher value with the increase of add-on. Also, the moisture regain of the treated silk fibers increased with add-on.