A recovery process of pure alumina powder from the wasted aluminum etching solution of electrolytic condenser works was studied. The possibility of this process was considered in the basis of thermodynamic data nad physico-chemical properties for the recovered materials were tested. In order to obtain pure alumina, Fe3+ and Cu2+ in the solution as impurities were solvent-extracted, respectively, and then, Al3+ was precipitated by changing the pH of the solution. As the results, more than 99.9% of Al3+ in the solution was recovered by the precipitation method. The weight of the precipitate was reduced to about 65 wt.% of the original one by calcination and the sizes of the recovered powders were in order of 3-5$mu extrm{m}$. The precipitates were transformed to $alpha$-Al2O3 at the calcination temperature about 120$0^{circ}C$.