The defect structure of calcium titanates with CaO excess or $TiO_2$ excess was studied by measuring electrical conductivities as a funcition of oxygen partial pressure at $85O^{circ}C$ to $1050^{circ}C$. Execess CaO may divide itself equally between A and B sites, resulting in $Ca_{Ti}$" and Vo", while excess $TiO_2$ form $V_{Ca}$" and Vo". The equilibrium electrical conductivity data indicate that the solubilities of CaO and $TiO_2$ in $CaTiO_3$ are 5000ppm and 2000ppm, respectively. Oxygen vacancies contributed to the ionic conduction which flatten the conductivity minima and did not make any defect association with oppositely charged defects.ely charged defects.