The crystalline character of NaOH and KOH-cellulose complex having different tension ratio was studied using X-ray diffraction analysis. Cellulose crystalline lattices in tension alkali treatment cotton were identified by measuring and indexing the 101, 101, and 002 reflections. According as alkali treatment tension ratio increased on, cellulose gave rise to the formation of I rather than cellulose II. It seemed that a part of the fine structure of cellulose increased orientation with antiparaell and parallel chain crystal structure. The high tension ratio alkali treatment cotton resulted in lower dye sorption and in higher breaking strength and crease recovery.