Graft polymers of alginic acid-PMMA, different in composition and Mv of branched PMMA, were prepared by emulsion graft polymerization at various MMA concentrations. In aqueous dispersion solution, the adsorption of graft polymer on the montmorillonite was carried out to modify the surface property of powder, and the adsorption of PMMA in organic solvents (acetone, benzene) on the modified surface of powder were observed. The results obtained were as follows. 1. In emulsion graft polymerization of MMA on the sodium alginate in aqueous solution, SA conversion, MMA conversion and % grafting were increased with increasing MMA concentration where as graft efficiency was decreased. 2. The adsorption amount of graft polymer was increased with the elevation of temperature and the increased of dispersion concentration and with the increase of branched PMMA composition of graft polymer. 3. In organic solvent, the adsorption of PMMA on the surface modified particle was proceeded by the orientation along the stretched branched PMMA of adsorbed graft polymer which is in radial direction to the particle surface. 4. The adsorbed amount of PMMA was increased as the temperature and concentration of PMMA solution, the branching of adsorbed graft polymer and the solvency of solvent were increased.