Pt loaded porous carbon Pt/C electrode was prepared by hot pressing process to enhance the electrode performance in PAFC (phosphoric acid fuel cell). By changing the hot pressing conditions and PTFE contents, Pt/C electrodes were prepared and the electrochemical characteristics of oxygen reduction and unit-cell performance were evaluated. The optimum condition of hot press to make electrode is 360$^{circ}C$ and 10 kg/$ extrm{cm}^2$. Maximum performance was obtained at 30 wt% PTFE content in the catalyst layer with 80% utilization of platinum clusters. Unit-cell performance of hot pressed Pt/C electrode was 200 mA/$ extrm{cm}^2$ at 700 ㎷ and stable performance was maintained more than 200 hr.