The purpose of this study was to evaluate the effect of the metal coping design on the fracture resistance of ceramometal crown. The Ni-Cr alloy(Supranium, Krupp Co., German) and Vaccm-fired porcelain powder(Vita VMK 689, Vita Co., Germany) were used in this study. The measurement of fracture resisitance of ceramometal crown was done with Instron Universial Testing Machine(Instro Co., Model no.4201). The obained results were as fellows : 1. The fracture resistance measured at the buccal cusp tip was the highest value in the group that those position of ceramometal junction was 2mm superior to the lingual finshing margin(100.25Kg) and the fracture resistance revealed on order of the group that those position was 2mm buccal to the central groove(51.64Kg). 2. The fracture resistance measured at the central groove was higher value in the group that those position was 2mm lingual to the central groove than in the group that those position was 2mm lingual to the central groove than in the group that those position was 2mm superior to lingual finishing margin(132.48Kg). 3. In all cases, the fracture resistance at the central groove was higher than that at the buccal cusp tip.