This paper aims to investigate the effect of B and Si upon the mechanical properties, microstructure and corrosion resistance of Co-Cr base alloy. Ten groups of alloy ingot ingot with various contents of B and Si were remelted by high frequency electrical induction furnace and cast into tensile specimen of ADA Specification No. 14 Tensile and hardness test were carried out by Amsler and Rockwell hardness tester(R-30N), respectively. The microstructures of specimen were observed by SEM. The results obtained are summarized as follows : 1. As B content is increased, tensile strength, yield strength and Rockwell hardness number(R-30N) are also increased significantly, while the elongation is decreased significantly. 2. As Si contect os increased, no significant chang in tensile strength is noticed, yield strength is slightly decreased, but Rockwell hardness number(R-30N) is moderately in creased, Elongation marks maxium value with 1% Si content while with more than 1% Si it is decreased. 3. As B content is increased corrosion resistance is decreased and is at best with 1.5% B content. Corrosion resistance is increased with the increase of Si content and the alloys with Si over 3.0% showed corrosion resistance. 4. As B content increased, precipitates are increased in number at grain boundaries. The grain size tends to become coarse with the increase of Si content. 5. Co rich-Cr alloy is present through matrix whereas at the grain boundaries Cr base precipitates are primarily formed.