Optimum hypering conditions are found for IIIa-J, IIIa-F, 103a-O, 103a-D, and IIa-O plates using hypersensitization machine in KAO. For every experimental plate we get speed gain, fog increment, signal to noise ratio and relative DQE according to hypering time and temperature. The hypersensitization method is baking with 8% hydrogen mixed gas. For IIIa-J, 103a-O, and 103a-D plates treated $65^{circ}C$, 3 hours baking, the speed gains arc increased by about 10 times, 2 times, and 2 times compared to untreated plates, respectively. The fogs are increased by 0.08, 0.10, and 0.08, respectively. For IIIa-F, IIa-O plates treated $65^{circ}C$, 2 hours baking, the speed gains are increased by about 4.7 times and 1.8 times compared to untreated plates, respectively. The fogs are increased by 0.15 and 0.04, respectively.