This study was undertaken to investigate the corrosive wear charateristics upon various transformation condition of austempered low-alloy ductile cast iron in corrosive environments against mating specimen made of the hardened SM45C. The corrosive wear test was carried out by rubbing the annular surface of two test pieces in distilled water and aqueous solution at constant sliding speed of 0.5m/s. In severe wear region, the corrosive wear rate Wc increased hastily with NaCl concentration owing to intermetallic adhesion but Wc went down slowly in mild wear region due to lubricating effect of the corrosion product. The critical sliding distance decreased with increasing NaCl concentration due to increased generation rate of the corrosion product and the specific corrosive wear rate has maximum in 1% NaCl aqueous solution at mild wear region. With the variation of matrix, the corrosive wear resistance of the fine acicular bainite was higher than that of coarse upper bainite because of reducing the local cell reaction by carbides. A growth in volume fraction of retained austenite in matrix increased the Wc due to soften surface, but has a declining tendency of Wc in mild wear region.