In this study, the electrical and optical properties of amorphous, crystallization and thin film of As-Ge-Se Chalcogenide System was investigated. Typical composition of this material has $As_{20~50}Se_{40~70} and Ge_{10~40}$ at%. Materials having Se was fixed to 40 at% and As was above 30 at% much more increased the electrical conductivity. After crystallization at the temperature of $476^{circ}C$ for 3 hour was showed the best electrical conductivity of 1.74E-13$(Omega cm)^{-l}$. And the main crystalline phase of this sample can be investigated using the mixed crystalline, i.e, $GeSe_2 and As_2Se_3$ phases. The thin film shows the optical absorption coefficient in the range $2{times}10^3 to 7{times}10^4$ and the optical energy gap of 1.85eV.