A study on optimizing the friction welding of copper(C1100) to aluminium(A1050) for developing the electrical sleeve was experimentally carried out and also on real-time nondestructive evaluation of the friction weld quality (strength) was accomplished by acoustic emission technique. The results obtained are summarized as the following ; 1) The heating upset $U_1$(mm) or total upset U(mm) tends to increase according to the increase of heating time $t_1$(sec). The relations between $U_1$ and $t_1$ or U and $t_1$are computed as follows when n=2000rpm, $P_1$=4, $P_2$=8kgf/$mm^2$, and $t_2$=6sec. U=1.6$e^{0.39t_1}$ $U_1$=3.65$e^{0.25t_1}$. 2) It was notified that the proper welding conditions by considering on both strength with more than 100% joint effieciency and toughness are heating time of 1.5-2.25 sec under n=200rpm, $P_1$=4, $P_2$=8kgf/$mm^2$, $t_2$=6sec. 3) It was confirmed that both AE total counts(N, counts) and the weld tensile strength (${sigma}$, kgf/$mm^2$) of the welded joints increase as the increase of heating time, respectively, the relations between N and $t_1$, ${sigma}$ and $t_1$ are computed from data points by regression analysis using the least square method as follows in case of the above proper condition ; N=50108+23917(ln $t_1$)${sigma}$$=11.85+2.06(ln $t_1$). 4) Both empirical and calcularated equations of relationship between .sigma. and N are very coincident with a high reliability, as the following in case of the above proper welding condition ; Calculated : ${sigma}$=0.00008N+7.5 Empirical :${sigma}$= $8.17e^{0.0000072N}$. 5) It was confirmed that the real-time nondestructive weld strength evaluation for friction welding of copper(C1100) to aluminium(A1050) could be possible by acoustic emission technique.