Chitin-based fibers have low mechanical strength and hence cannot be used as surgery fiber due to fast degradation In tissues. A new fiber Chitulose was made by mixing chitin with cellulose, both of which have similar structure. A mixture of dimethylacetamide (DMAc) and 6% lithium chloride (LiCl) was found to be an effective solvent system for dissolvoing chitin and cellulose. The Chitulose fiber made by wet spinning of a mixture of chitin and cellulose resulted in the highest degree of strength and flexibility when the ratio of chitin to cellulose was 1.5; 0.2. The fiber maintained mechanical structure even after autoclaving, indicating thermal stability. A biodegradability test of the Chitulose fiber by imbeding in a rat showed that degradation was initiated in 14 days and completely done in 40 days.