Sintering behaviour of zirconia powders prepared by different processing treatment was discussed. About >99% densities of theoretical were obtaiend on sintering at 140$0^{circ}C$ for 2h in case of 300MPa uniaxially cold-pressed compact. But the lower densities were obtained on sintering above this temperature due to abnormal grain growth enabling the tetragonal to monoclinic phase transformation during cooling resulted in microcracks. All kinds of different dried powders exhibited nearly the same shrinkage behaviour with end-point shrinkage between 19 and 20%, and had maximum shrinkage rate (0.99~1.27%/min) around 120$0^{circ}C$. During whole sintering process densification was mainly governed by grain growth and rearrangement of agglomerates. Heterogeneous abnormal grain growth and abrupt decrease in shrinkage were observed when continuous interagglomerate pore collapsed into isolated pores.