Effects of microstructures on the electrical properties of ZrO2 based ceramics were analyzed by modeling layer arrangements and mixed phase structures. Single layers and alternating multilayers were made from 3mol% and 8mol% Y2O3 doped ZrO2 powders, while mixed specimen was made by blending and compacting these raw powders. After sintering at 150$0^{circ}C$ for 2hr in air, AC impedance characteristics were measured. Contributiion of bulk comonent to total resistivity and its temperature-dependence were larger in 8Y-ZrO2 single layer than in 3Y-ZrO2 single layer. The multilayered specimen connected in serial to electrodes showed partial characteristics of both 3Y-ZrO2 and 8Y-ZrO2 single layers. The multilayered specimen connected in parallel to electrodes and the mixed specimen exhibited characteristics mainly of 8Y-ZrO2 single layer. The multilayered specimen connected in parallel to electrodes revealed the highest electrical conductivity near the operating temperature of solid oxide fuel cell. However, it is expected that the mixed specimen is appropriate for the applications because of its relatively high electrical conductivity with high strength expected.