Electrical and mechanical properties of Pb(Mg, Te, Mn, Nb)O3-PZT ceramics are investigated as a function of CeO2 addition (0 to 0.3wt%), and the output characteristics of piezoelectric transformer are also presented. The grain size decreased and the shapes of particles were more uniform with the addition of CeO2. The coercive electric field(9500V/cm), mechanical quality factor (2500) and bend strength (1065kg/$ extrm{cm}^2$) were improved by addition of CeO2 0.2wt%. After repetition of a number of stress cycles, the degradation of k33 was not found in this sample. The voltage step-up ratio (Vdc/Vrms) of piezoelectric ceramic transformer (half wavevoltage doubler, load resistor 100M.ohm) was about 950 in a linear region, its value was relatively higher than other materials.