The electro-magnetic properties of the Mn-Zn ferrite single crystal with small variation of Fe2O3 concentration at the high permeability composition, 53mol% Fe2O3-28.5mol% MnO-18.5mol% ZnO, have been studied for the VCR magnetic head application. With the increase of the Fe2O3 concentration, the Fe2+ concentration increased, the specific resistivity decreased, the secondary maximum permeability shifted to the lower temperature, and the initial permeability decreased. It was concluded that the small variation of $pm$0.5mol% Fe2O3 concentration greatly affected the electro-magnetic properties of Mn-Zn ferrite single crystals. At the composition of 53mol% Fe2O3, the initial permeability was comparatively high (650 at 5MHz) and its temperature dependence was small.