YBa2Cu3Ox(YBCO) thick films were prepared by a screen printing of the powders, obtained by a coprecipitation in oxalic acid, on the Y2O3-stabilized zirconia substrates and their superconducting properties were determined. TC, JC and the orientation factor of the thick films increased with increasing temperature up to 103$0^{circ}C$ and then the superconducting properties disappeared with further heat treatments. The optimization of JC was achieved by heating thick films at 103$0^{circ}C$ for 7min. In this case the TC of the thick film was determined to be 87.5K. It was observed that TC of thick films depends on the orthorhombicity and JC is likely governed by a microstructure of YBCO rather than by the orientation factor.