The general requirements of recording media include recording performance, environmental stability, runnability on the drive or deck, and manufacturability. CoCrMo thin films were prepared using RF sputtering system for a study on chemical stability. Surface degradation of the CoCrMo thin film was studied by SEM, XPS and AES. Surface degradation was found to be dependent of sputtering condition and Mo content. Addition of Mo to CoCr thin film improved dramatically its surface degradation resistance in dilute sulfuric acid, as indicated by active-passive transition appeared in electrochemical polarization curve. Futhermore, the passive current density was decreased with increasing Mo content. The reduction in a number density of corrosion sites by Mo addition vms observed, after accelerated corrosion test. AES survey indicated that corrosion occured on the site with Cr depletion and highly concentrated chloride ions.