Cd4SnSea6 & Cd4SnSe6 : Co2+ single crystals were grown by the chemical transport reaction (CTR) method. The grown single crystlas crrystallize in the monoclinic structrue and have the direct band gaps. The energy gaps of them are 1.68eV for Cd4SnSea6 & Cd4SnSe6 : Co2+ at 293K. The impurity opticla absorption peaks due to cobalt dped with impurity appear at 4879cm-1, 5392cm-1 and 6247 com-1, and are attributed to the electron transitions between the split energy levels of Co2+ ion sited at Td symmetry of Cd4SnSe6 single crystal.