The purpose of this study was to evlauate the microleakage of 3 dentin bonding agents using different dentin pretreatment method under simulated physilogic pressure in cementing the porcelain laminate veneer. Noncarious 60 human maxillary molars were selected and randomly assigned to 4 groups of 15 each. The group with the margin placed on the enamel was classified as the control and the groups with the margin placed on root surface were subdivided into 3 groups according to the dentin bonding agents used. The group using All Bond 2 was classified as experimental group 1, the group using Scotchbond MP was classified as experimental group 2, and the group using Gluma was classified as experimental group 3. Roots were removed at 3mm below the cementoenamel junction, and reductions of the teeth for the porcelain laminate veneer were done on the mesial 1/2 of the buccal surface of each teeth. The pulp was extirpated and the pulp chamber was cleaned with 37% phosphoric acid for the patency of dentinal tubule. Under simulated physiologic pressure, porcelain laminate veneers were cemented to the teeth using each dentin bonding agent and luting cement. After cementation, all samples were stored at 36t in water for 24 hours and thermocycled for 1500 cycles, then immersed in 0.5% basic fuchsin solution and the teeth were sectioned longitudinally by using diamond saw and the extent of microleakage was measured. The following results were obtained, 1. Microleakage was observed in a few samples of control group but all the samples of experimental groups. 2. The control group showed the less extent of microleakage than the experimental groups. In experimental groups the experimental group 1 & the experimental group 2 showed similiar extent of microleakage and the experimental group 3 showed the greater extent of microleakage than other groups. Conclusively, practicing the porcelain laminate veneers in the clinic, although the margin of the porcelain laminate veneer should be placed on enamel, in the case that it is inevitable to place the margin of the porcelain laminate veneer on the root surface, it is recommened to use dentin bonding agents which use no dentin pretreatment or a dentin pretreatment which can leave the smear plugs.