A study on corrosion and adhesion properties of evaporated Zn-Cr films were conducted on steel strip by two-source evaporater. Corrosion resistance of Zn-Cr coated steel was evaluated by salt spray test in 5% NaCl. Adhesion property of Zn-Cr films on steel substrate was evaluated by tape test after $180^circC$ bending. Adhesion was improved with increasing the Cr content and reached the maximum at the Cr content of 6 to 8wt%. Corrosion resistance was enhanced with increasing the Cr content and improved by rolling Zn-Cr coated specimen, as a post-treatment.