In this experiment, to find optimum brazing conditions for Cu/Stainless Steel brazing using filler metals of Ag-Cu-Zn-Cd system, first of all spreading ratio was tested on 304 stainless Steel and low carbon steel. And then shear test of brazed joint was executed. As the result of that, the shear strengths of brazed joints were the range of 60-90 MPa. Through microstructure analysis for brazed interface layer, We found as follows. Firstly interface layer increased as time increased. Secondly continuous layer of Ag-Cd compound was observed along the side of stainless steel. Also by means of EDS analysis for fracture surface, ductile fracture was occurred and precipitates on the fracture surface were found to include Cr, Mn, Si in Ag-rich phase.