An experimental study on heat transfer and flow in compression molding of clss-B and A SMC(Sheet Molding Compounds) in a flat plate and a cross-sectional T-shape was carried out. The temperature was measured with thermocouples at two locations in the 4 layered SMC charge and pressure was measured at the center of the top mold during compression molding. Three different mold speeds, 15, 45, 50 mm/min and two different mold temperature, $130^{circ}C{;}and{;}150^{circ}C$ were used for compression molding experiments. Experiments with different colored SMC layers were used to study flow patterns at various compression stages. In oder to predict the pressure and load in SMC compression molding, slab method was used. The predicted values of pressure and load from the slab analysis were compared well with the measured data.